Leak detection in vacuum bags

ABSTRACT

A device indicates the location of an air leak in a vacuum bag used to process composite parts. The device includes a layer of material on the inner face of the bag that changes in appearance due to an oxidation-reduction reaction in areas of the layer exposed to oxygen caused by a leak in the bag.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is related to co-pending U.S. patent application Ser. No. 11/829,900 filed Jul. 28, 2007, which is incorporated by reference herein in its entirety.

TECHNICAL FIELD

This disclosure generally relates to techniques and equipment for detecting leaks in vacuum bags used in manufacturing processes, such as the curing of composite layups, and deals more particularly with a method and device that allows leak detection through visual observation.

BACKGROUND

Flexible vacuum bags are often used to compact and consolidate composite part layups during curing. These bags comprise an oxygen impermeable film such as nylon which sometimes develops leaks during the curing cycle. Bag leaks are difficult to detect and, if not quickly repaired, may result in parts that do not exhibit the desired mechanical properties.

A variety of techniques and equipment have been devised in the past to detect leaks in vacuum bags, but each may have disadvantages. For example, known leak detection techniques may require specialized equipment and/or operators, may be time consuming, may be less than completely reliable and/or may be impractical to use on relatively large parts.

One known technique for detecting bag leaks is performed by moving an ultrasonic listening device over the surface of a part. Leaking air may often cause a high pitch noise that can be detected by the listening device in order to identify the location of the leak. Another known leak detection technique uses helium leak detection equipment comprising a helium source and a helium detector. The helium source is moved slowly over the surface of the bag, while the helium detector is used to sense helium traveling from the source through the bag leak, thereby marking the location of the leak.

In the food industry, colorimetric dyes have been used to detect air leaks in food packages in order to provide an indication that the packaged foods may be subject to spoilage. These colorimetric dyes are in the form of ink that is applied inside the food packaging, and which change color on exposure to oxygen, thereby providing a visual indication that the package contains a leak.

Accordingly, there is a need for a method and device for detecting leaks in vacuum bags used to process composite parts such as composite layups that avoids the need for specialized detection equipment and which provides a rapid visual indication of the location of bag leaks.

SUMMARY

The disclosed embodiments provide a method and apparatus for detecting leaks in flexible film bags used to process parts in industrial applications such as vacuum bag processing employed to compact and consolidate composite layups during curing, or to bond parts together. The method may also be used to detect leaks in substrates such as tools and other parts. The method relies on a color change in the bag that can be readily detected with the naked eye and therefore does not require detection equipment. A colorimetric material in the form of an ink or dye is applied to the inner face of the vacuum bag film. The ink exhibits a substantially homogeneous color prior to being activated. After the part is placed on a cure tool and covered with the vacuum bag, the bag is sealed to the tool. A vacuum is then drawn within the bag, causing the air pressure within the bag to drop, which then allows the atmospheric pressure to push the bag down onto the layup and compact the layup. The colorimetric material is activated by directing UV (ultraviolet) light through the transparent bag onto the ink. The incident UV light activates the ink, changing its color and rendering it reactive to oxygen. Following activation, the material exhibits localized changes in color when exposed to oxygen due to a leak.

According to one disclosed embodiment, a device is provided for indicating the location of an air leak in a vacuum bag used to compact composite parts. The device comprises a layer of material on the inner face of the bag that changes appearance due to an oxidation-reduction reaction in areas of the layer exposed to oxygen caused by a leak in the bag. The layer of material may comprise a colorimetric ink including an oxygen permeable binder having semi-conductor nanoparticles dispersed therein. The material may further include an electron-donor material and a reduction-oxidation indicator material.

According to another embodiment, apparatus is provided for compacting a composite part, comprising a tool adapted to have the composite part placed thereon and a substantially transparent, gas impermeable film forming a bag adapted to be placed over the part and sealed to the tool. The apparatus further includes a selectively activatable, colorimetric ink on the inner face of the film for providing a visual indication of the location of any air leaks in the film. The apparatus also includes a vacuum source for drawing a vacuum within the bag, and a radiation source for directing radiation through the film onto the colorimetric ink for activating the ink after the vacuum has been drawn in the bag. The radiation source emits radiation generally within the ultraviolet band of wavelengths.

According to a further embodiment, a method is provided of detecting leaks in a transparent vacuum bag used to process parts. The method comprises applying a layer of material on the inner face of the bag that changes appearance in the area of an air leak in the bag, and visually observing changes in the appearance of the layer of material viewed through the bag. The method may further comprise activating the layer of material to become reactive to oxygen in the air entering the bag through the leak.

According to one disclosed embodiment, a method is provided of detecting leaks in a substrate. The method comprises applying a layer of material to an interior face of a substantially transparent bag and sealing the bag over the substrate. The material is activatable to an oxygen reactive state in which the color of the material changes in response to the exposure of the material to oxygen. The method further comprises generating a vacuum within the bag and activating the layer of material to its oxygen reactive state, following which leaks in the substrate may be detected by visually observing localized changes in the color of the material. The layer of material may be activated by subjecting the layer to UV light for a predetermined length of time.

According to another embodiment, a method is provided of processing a part, comprising providing a material that may be activated from a first state in which the material exhibits a first color, to a second state in which the material exhibits a second color that reverts substantially to a color when exposed to oxygen. The method further includes applying a layer of the material in its first state on an inner face of the oxygen impermeable film and placing the film over the part with the inner face of the film facing the part. The method also includes sealing the film around the part to form a vacuum chamber and drawing a vacuum within the chamber, following which the material may be activated from the first state to the second state. Air leaks in the film may be detected by visually observing a localized change in color in the layer of material. Activating the material is performed after the vacuum has been drawn. The activation of the material may be performed by directing UV light through the film onto the layer of material.

The disclosed embodiments provide a method and apparatus for detecting leaks in vacuum bags which is relatively quick, reliable and is not highly dependent upon sophisticated equipment to identify the location of leaks.

BRIEF DESCRIPTION OF THE ILLUSTRATIONS

FIG. 1 is an illustration of a cross sectional view of a portion of a vacuum bag assembly used to compact a composite part layup.

FIG. 2 is an illustration similar to FIG. 1, but exploded to better show the components of the assembly.

FIG. 3 is an illustration of the area designated as “A” in FIG. 2, and showing a layer of colorimetric ink having been applied to the inner face of the bag.

FIG. 4 is an illustration of a view similar to FIG. 3 but showing a UV light source radiating ultraviolet light through the bag onto the layer of colorimetric ink.

FIG. 5 is an illustration of a view similar to FIG. but showing the layer of colorimetric ink having been activated to an oxygen sensitive state.

FIG. 6 is an illustration of a view similar to FIG. 5 but showing a leak in the bag.

FIG. 7 is an illustration of a view similar to FIG. 6, but showing the layer of colorimetric ink exhibiting a visible color in the area of the leak.

FIG. 8 is an illustration of the outer face of the bag taken in a direction designated as “B” in FIG. 7.

FIG. 9 is an illustration similar to FIG. 1, showing a leak in the tool allowing air to enter the vacuum chamber.

FIG. 9A is an illustration similar to FIG. 9, but showing use of a vacuum bag having colorimetric material to test a tool substrate for air leaks.

FIG. 10 is an illustration useful in explaining activation of the colorimetric which includes an oxidation-reduction reaction.

FIG. 11 is an illustration useful in explaining how the absorbsion of UV light by the colorimetric layer of ink creates electron-hole pairs which promote the oxidation-reduction reaction.

FIG. 12 is an illustration of a flow diagram showing the overall steps of a method of leak detection in vacuum bags.

FIG. 13 is an illustration of a flow diagram of aircraft production and service methodology.

FIG. 14 is an illustration of a block diagram of an aircraft.

DETAILED DESCRIPTION

Referring first to FIGS. 1 and 2, a vacuum bag assembly 20 comprises a gas impermeable, substantially transparent vacuum bag 30 adapted to cover a part, such as a composite part layup 22 that is supported on a tool 24. The bag 30 is sealed around its periphery to the tool 24 by means of a peripheral seal 32 that extends around the perimeter of the part layup 22. The assembly 20 may further comprise any of various additional layers of material above or below the part layup 22, such as, without limitation, a release film 26 and a breather 28. The vacuum bag 30 may comprise a flexible film such as, for example and without limitation, nylon, that is coupled with a suitable vacuum source 34 for drawing a vacuum within the bag 30. A vacuum is drawn within the bag 30, causing the air pressure within the bag 30 to drop, which then allows the atmospheric pressure to push the bag 30 down onto the breather 28 and the layup 22. The atmospheric pressure pushing the bag 30 down applies compaction pressure to the layup 22 which assists in consolidating and compacting the layup 22 during the curing process. Although not specifically shown in FIGS. 1 and 2, one or more leaks may occur in the bag 30 which desirably should be detected as early as possible during the curing and/or compaction process, so that the bag 30 can be repaired or replaced before the part layup 22 is fully cured and/or compacted. In accordance with the disclosed embodiments, such leaks may be detected by visual observation with the naked eye, without the aid of equipment.

Referring now to FIG. 3, a layer of leak detection material 36, sometimes also referred to herein as a layer of colorimetric material, colorimetric ink or a colorimetric dye, is disposed between the inner face 30 a of the bag 30, and the part layup 22. In the embodiment illustrated in FIG. 3, the layer of colorimetric material 36 is adhered to the inner face 30 a of the bag 30, however in other embodiments, the colorimetric material 36 may be coextruded with the film from which the bag 30 is made so that it forms an integral part of the bag 30. In still other embodiments, the colorimetric material 36 may be applied to or integrated into an extruded film (not shown) that is separate from the bag 30.

The colorimetric material 36 comprises a mixture of an oxygen permeable polymer which functions as a binder, a dispersion of photoactive semiconductor nanoparticles held in the binder, a material that functions as an electron donor, and a material that acts as a reduction-oxidation (hereinafter “redox”) indicator. The polymer binder may comprise, for example and without limitation, hydroxyethyl cellulose (HEC), and the semiconductor nanoparticles may comprise, for example and without limitation, a photo-active metal oxide such as TiO₂ (titanium dioxide). The electron donor material may comprise, for example and without limitation, glycerol, ascorbic acid or hydrazine and the redox indicator (reducing agent) may comprise without limitation, indigo-tetrasulfonate (ITS), methylene blue or dimethylmethylene blue.

Photoactive metal oxides are incorporated into the colorimetric material 36 in order to provide electron transport for the oxidation of the ITS. In its oxidized form, ITS is substantially colorless. The metal oxides suitable for the present application may exhibit arrangement of energy levels in the form of a band gap. The band gap is the difference in energy between the valance band where most of the electrons reside, and the conduction band which is a band of partially or completely unoccupied energy levels. In order for band gap materials to be photoactive, the energy gap between the valance and conduction bands of the material must equal the energy of a photon. TiO₂, for example, has a band gap energy of approximately 3.18 electron volts. This energy difference corresponds to a photon of 387 nm. Therefore, illumination of TiO₂ with 387 nm light will populate the conduction band with electrons.

Another feature of band gap materials is that the orbitals of the outer electrons on individual atoms will overlap each other, resulting in a delocalization of electrons. As a result, the electrons will exhibit some mobility among those orbitals that they partially occupied. The mobility or conductivity of electrons in the metal oxide effects the oxidation of the ITS redox indicator. In addition to TiO₂, other metal oxides that have band gaps satisfying the requirements for UV light excitation from a valance band to the conduction band may be employed in the ink 36. These materials include, but may not be limited to silicon carbide (SiC), zinc sulfide (ZNS), gallium nitride (GaN) and tantalum oxide (Ta₂O₅).

In one typical application, the colorimetric material 36 comprises an ink that may be prepared by the following process. A 5% HEC solution (i.e. 5 grams of HEC per 100 grams of water) is prepared, to which 0.2 grams of glycerol are added. An admixture of 0.02 grams of P25 photoactive metal oxides are incorporated into the bag film to provide electron transport for the oxidation of the ITS. TiO₂ and 0.005 grams of ITS are added to the solution of HEC and glycerol. The mixture is sonicated for approximately 15 minutes or stirred using a high speed mixer with a rotor stator attachment.

The colorimetric ink formulation described immediately above may be applied to the inner face 30 a of the vacuum bag 30 by any of several techniques including, but not limited to printing, spin-casting or spraying. Alternatively, the colorimetric material 36 may be incorporated into the film forming the vacuum bag 30 by coextruding the material 36 along with the vacuum bag film, as mentioned previously. Additional details of suitable colorimetric materials and techniques for their preparation are described in the following publications which are incorporated by reference herein in their entireties: Andrew Mills, C. Tommons, R. Bailey, M. Tedford and P. Crilly, “UV-Activated Luminescence/Colourimetric O1 Indicator”, International Journal of Photoenergy, Volume 2008, pp 2-6; and S. K. Lee, M. Sheridan and A. Mills, “Novel UV-Activated Colorimetric Oxygen Indicator”, Chemistry of Materials, volume 17, no. 10, pp 2744-2751, 2005.

When initially applied to the bag 30 as described above, the layer of colorimetric material 36 exhibits a visible color largely determined by the material selected as the redox indicator. In the illustrated example the redox indicator comprises ITS which is relatively dark blue in color. Other colors may be possible, depending upon the material selected as the redox indicator. As used herein, the term “color” is intended to include all of the colors within the visible spectrum, including black and white. The term “colorless” is intended to mean substantially without color or substantially transparent. As initially applied in the illustrated example, the colorimetric material 36 employing ITS as the redox indicator has a relatively dark blue color, which can be visually observed through the transparent vacuum bag 30.

As will be discussed below in more detail, after the vacuum bag 30 is installed and evacuated of air, the colorimetric material 36 is “activated” by irradiating the material 36 with radiant energy of a suitable wavelength for a preselected period of time. The radiation may comprise, without limitation, UV (ultraviolet) light 38 generated by a UV light source 40. UV light comprises electromagnetic radiation having a wavelength generally in the range of approximately 10 nm to 400 nm, and energies from about 3 eV to 124 eV. In one practical example, use of UV light having a wavelength of approximately 390 nm yielded satisfactory results. The layer of colorimetric material 36 is irradiated with the UV light for a length of time sufficient for the material 36 to become substantially colorless, which in one example, requires approximately 30 seconds of applied UV light having a wavelength of 390 nm.

Prior to activation, the colorimetric material 36 exhibits the initial color of the redox indicator and is substantially non-reactive to oxygen. However, once activated by the UV light 38, the material 36 changes in appearance either to a different color or to a substantially colorless state in which it is reactive to oxygen. FIG. 5 illustrates the layer of colorimetric material 36 following activation by UV light 38, in which the material 36 is substantially colorless or transparent. Since the bag 30 remains evacuated and thus free of oxygen while the part layup 22 is curing, the colorimetric material 36 remains in its “activated” colored or colorless state unless and until it is exposed to oxygen as a result of a leak in the bag 30. As will be discussed below in connection with FIGS. 6-8, those areas of the material 36 that are exposed to oxygen as result of a leak exhibit a localized color change. This color change may comprise a change from a substantially colorless state, to a state in which the material 36 exhibits a color (which may or may not be the color of the material 36 prior to its activation) or from the color to which the material was activated to a different color. For example, after activation with UV light, an ITS that is initially blue but changes to a colorless state when activated by UV light, may change from colorless to green when exposed to oxygen. Regardless of the exact color to which the material changes after exposure to oxygen, the color change is readily visible to an operator without the aid of specialized equipment.

Referring now to FIGS. 6-8, a leak 42 in the bag 30 allows oxygen-containing air to flow through the leak 42, as indicated by the arrows 44. At the bottom 45 of the leak 42, near the inner face 30 a of the bag, the incoming air increases the internal air pressure in the bag immediately surrounding the leak 42, allowing air to be redirected laterally as shown by the arrows 44 a for a distance determined at least in part by the amount of pressure being applied by the bag 30 to the substrate 22.

As shown in FIG. 7, the portion 46 of the colorimetric material 36 surrounding the leak 42 reverts from a colorless state to a colored state upon exposure to the oxygen in the air drawn into the bag 30 through the leak 42. The “colorizing” or change in color of the material 36 in the area 46 surrounding the leak 42 is visible to the naked eye 48 through the transparent bag 30, thus allowing an operator to quickly see through visual observation the particular location of the leak 42. Depending upon the amount of pressure applied to the part layup 22 by the bag 30, the concentration of oxygen reaching the layer of colorimetric material 36 may be somewhat graduated with increasing lateral distance from the leak 42. Thus, as shown in FIG. 8, the intensity of the color appearing in the exposed area 46 of the material may be graduated, with the areas 46 a immediately surrounding the leak 42 being darker than those in the outlying areas 46 b.

The colorimetric material may also be effective in detecting air leaks in other parts of the vacuum bag assembly 20 that cause an undesirable increase of air pressure within the bag 30. For example, as shown in FIG. 9, an air leak 42 may occur in the tool 24 which allows air 44 to enter the vacuum chamber formed over the layup 22. In accordance with the disclosed embodiments, the oxygen contained the air flowing in through the leak 42 is sensed by the layer of colorimetric material 36 on the inner face 30 a (FIG. 7) of the bag 30. As previously described, the colorimetric material 36 reacts to the oxygen introduced through the leak 42 by changing its color display, and this change in localized color display may be visually seen through the transparent bag 30 by an operator without the aid of specialized equipment. As illustrated by this example, the colorimetric material 36 may be used to detect air leaks in a variety of underlying substrates, including but not limited to tools used in processing composite parts. Thus, as shown in FIG. 9A, the use of the colorimetric material 36 inside the bag 30 may be employed according to the disclosed embodiments to test a tool 24 or other part or substrate for possible leaks before the tool 24 is placed into use in processing parts such as the layup 22. In order to carry out such testing, the bag 20 having an applied layer of the colorimetric material 36 is sealed to the tool 24, but without placing the layup 22 or other part on the tool 26. A vacuum is then drawn within the bag 30, causing the air pressure within the bag 30 to drop, which then allows the atmospheric pressure to push the bag 30 down onto the tool surface 28. After the colorimetric material 36 is activated with UV light 38, an operator may detect leaks 42 in the tool 24 by visually observing any color changes that may occur in the material 36 seen through the transparent bag 50.

It should be noted here that while the use of the colorimetric material 36 to detect air leaks has been described in connection with vacuum bag curing of composite layups, it may also be used in other applications where vacuum bags are employed in industrial processes. For example, the colorimetric material 36 may be used to detect leaks in vacuum bags that are used to apply compaction pressure to two or more parts (not shown) that are being bonded together with an adhesive.

Attention is now directed to FIGS. 10 and 11 which diagrammatically illustrate the physical and chemical reactions involved in the activation of the colorimetric material 36 and the related color changes in the redox indicator following activation and subsequent exposure to oxygen as a result of a bag leak. As previously stated, prior to activation, the material 36 may be typically be deeply colored. Irradiation of the ink 36 with UV light 38 (FIG. 9) results in excitation of the TiO₂ semiconductor 50 where electron-whole pairs e⁻, h⁺ are created.

The absorption of the UV light 38 by the semiconductor 50 results in the promotion of an electron e⁻ from the valence band 66 (FIG. 10) of the semiconductor 50 to its conduction band 68. When the electron e⁻ is promoted to the conduction band 68, it also creates an electron hole h⁺ that contains a positive partial charge. The hole h⁺ promotes the oxidation of the electron donor, which in the illustrated example is glycerol 52 that is irreversibly oxidized to glyceraldehyde 54. The photo-generated electrons e⁻ in the semiconductor 50 represented at 56 also reduce the redox indicator, which in the illustrated example is represented by “ITS (reduced)” and designated by the numeral 58. In its reduced or LEUKO form 58, the ITS redox indicator is substantially colorless and remains so in the absence of oxygen. However, when exposed to oxygen, the redox indicator oxidizes back to its colored form represented as “ITS (oxidized)” 60. This redox reaction also converts the O₂ to H₂O. It should be noted here that the ink 36 can be reused by repeated application of UV light 38 and that a variety of differential color changes and sensitivities are possible.

Attention is now directed to FIG. 12 which illustrates the overall steps of a method of detecting leaks in vacuum bags using human visual observation. Beginning at step 70, a colorimetric material 36 is applied to the inner face 30 a of a substantially transparent, flexible bag 30 using any of the application processes previously described. Next, at step 72, the bag assembly is prepared which may include assembling the bagging materials such as a release film 26, part layup 22, breather 28 and bag 30 (FIGS. 1 and 2). At step 74, the bag 30 is sealed to the tool 24, creating a substantially air tight vacuum chamber over the part layup 22 following which, a vacuum is drawn in the bag at 76 at step 78 which evacuates the bag of air.

At step 78, the bag is irradiated with UV light which passes through the transparent bag onto the colorimetric ink 38. The colorimetric ink 38 is irradiated with the UV light until the ink 36 changes color or becomes substantially colorless or transparent, thereby activating the material 36 as an oxygen sensor. At step 80, an operator visually monitors the bag for localized appearances of color or changes in color indicative of a possible leak. At step 82, local appearances of color or changes in color in the bag may be detected by the operator indicating the presence of an air leak in the bag. Upon detection of an air leak, an operator may repair or replace the bag, as shown at step 84.

Embodiments of the disclosure may find use in a variety of potential applications, particularly in the transportation industry, including for example, aerospace, marine and automotive applications. Thus, referring now to FIGS. 13 and 14, embodiments of the disclosure may be used in the context of an aircraft manufacturing and service method 86 as shown in FIG. 12 and an aircraft 88 as shown in FIG. 14. Aircraft applications of the disclosed embodiments may include, for example, a wide variety of composite structural components, assemblies and subassemblies. During pre-production, exemplary method 86 may include specification and design 90 of the aircraft 88 and material procurement 92. During production, component and subassembly manufacturing 94 and system integration 96 of the aircraft 88 takes place. Thereafter, the aircraft 88 may go through certification and delivery 98 in order to be placed in service 100. While in service by a customer, the aircraft 88 is scheduled for routine maintenance and service 102 (which may also include modification, reconfiguration, refurbishment, and so on). The disclosed embodiments may be employed to carry repairs requiring bonding of parts during the maintenance and service 102.

Each of the processes of method 110 may be performed or carried out by a system integrator, a third party, and/or an operator (e.g., a customer). For the purposes of this description, a system integrator may include without limitation any number of aircraft manufacturers and major-system subcontractors; a third party may include without limitation any number of vendors, subcontractors, and suppliers; and an operator may be an airline, leasing company, military entity, service organization, and so on.

As shown in FIG. 14, the aircraft 88 produced by exemplary method 86 may include an airframe 104 with a plurality of systems 106 and an interior 108. Examples of high-level systems 106 include one or more of a propulsion system 110, an electrical system 112, a hydraulic system 114, and an environmental system 116. Any number of other systems may be included. The disclosed method and device may be employed to fabricate structural components used in the airframe 104 and assemblies or subassemblies used in the interior 108. The embodiments may also be used to bond components forming part of the interior 108 or the airframe 104. Although an aerospace example is shown, the principles of the disclosure may be applied to other industries, such as the marine and automotive industries.

Systems and methods embodied herein may be employed during any one or more of the stages of the production and service method 86. For example, assemblies or subassemblies corresponding to production process 94 may be fabricated or manufactured in a manner similar to components or subassemblies produced while the aircraft 88 is in service. Also, one or more apparatus embodiments, method embodiments, or a combination thereof may be utilized during the production stages 95 and 96, for example, by substantially expediting assembly of or reducing the cost of an aircraft 112. Similarly, one or more of apparatus embodiments, method embodiments, or a combination thereof may be utilized while the aircraft 112 is in service, for example and without limitation, to maintenance and service 102.

Although the embodiments of this disclosure have been described with respect to certain exemplary embodiments, it is to be understood that the specific embodiments are for purposes of illustration and not limitation, as other variations will occur to those of skill in the art. 

What is claimed:
 1. A device for indicating the location of an air leak in a vacuum bag assembly used to compact composite parts, comprising: a sheet of the vacuum bag, the sheet having an inner face, the bag receiving a vacuum applied on the inner face, the vacuum bag positioned over a tool; and a material incorporated into the vacuum bag such that the material is integral with the vacuum bag, the vacuum bag and material forming a single layer, the material configured to transition from a first color to a second color upon activation, and from the second color to a third color due to an oxidation-reduction reaction in areas of the material exposed to oxygen, the material comprising an oxygen permeable polymer binder, semiconductor nanoparticles dispersed in the binder, an electron donor material, and a reduction-oxidation indicator material, the material configured to transition to the third color upon air leaking into the vacuum bag assembly through the vacuum bag, through the tool, or through the vacuum bag and the tool wherein the first color is blue, the second color is colorless, and the third color is green.
 2. The device of claim 1, wherein the material is an ink that changes from a substantially colorless state to a color in the exposed areas of the layer as a result of the oxidation-reduction reaction.
 3. The device of claim 1, wherein the semiconductor nanoparticles are one of TiO₂,SiC, ZnS, GaN, and Ta₂O₅; the electron donor material is glycerol; and the reduction-oxidation indicator material is indigotetrasulfonate.
 4. The device of claim 1, wherein the material is a printed ink.
 5. The device of claim 1, further comprising a radiation source configured to emit the ultraviolet light.
 6. The device of claim 1, further comprising a vacuum source for drawing a vacuum in the vacuum bag.
 7. The device of claim 1, wherein the first color is blue, the second color is colorless, and the third color is green.
 8. The device of claim 1, wherein the leak is through the tool.
 9. A method of detecting leaks in a transparent vacuum bag used to process parts, comprising: incorporating a material into the bag, the material being integral with the bag so that the material and the bag form a single layer, and configured to change appearance in the area of an air leak in the bag, the material comprising an oxygen permeable polymer binder, semiconductor nanoparticles dispersed in the binder, an electron donor material, and a reduction-oxidation indicator material; positioning the bag over a tool; evacuating air from the bag; activating the material with UV light to form an activated material such that the material transitions from a first color to substantially transparent, the activated material configured to react with oxygen in the air entering the bag through a leak and thereby to transition to a third color, the third color being a visible color, wherein the first color is blue, the second color is colorless, and the third color is green; and visually observing for changes in the appearance of the layer of material viewed through the bag caused by an air leak through the bag, through the tool, or through the bag and the tool.
 10. The method of claim 9, wherein activating the material is performed after the bag has been substantially evacuated of air.
 11. The method of claim 9, wherein the step of incorporating the material comprises co-extruding the material into the bag such that the material is integral with the bag.
 12. The method of claim 9, wherein the first color is blue and the third color is green.
 13. The method of claim 9, wherein the leak is through the tool.
 14. A method of detecting leaks in a substrate, comprising: incorporating a material into a substantially transparent bag such that the material is integral with the bag in a single layer, the material configured to transition from a first color to a second color with activation by UV light, the second color corresponding to an oxygen reactive state in which the second color of the material is further configured to change to a third color in response to the exposure of the material to oxygen, wherein the first color is blue, the second color is colorless, and the third color is green, the material comprising an oxygen permeable polymer binder, semiconductor nanoparticles dispersed in the binder, an electron donor material, and a reduction-oxidation indicator material; sealing the bag over the substrate; generating a vacuum within the sealed bag; activating the material to its oxygen responsive state with UV light; and detecting leaks in the substrate by visually observing for localized changes in the color of the material.
 15. The method of claim 14, wherein incorporating a material is performed by co-extruding the material along with the bag such that the material is integral with the bag.
 16. The method of claim 14, wherein activating the material is performed after the vacuum has been generated within the bag.
 17. The method of claim 14, wherein subjecting the material to UV light includes passing the light through the transparent vacuum bag.
 18. The method of claim 14, wherein the step of sealing further comprises placing a composite part on the substrate and sealing the bag over the composite part on the substrate.
 19. The method of claim 14, wherein the step of activating further comprises emitting ultraviolet light from a radiation source.
 20. The method of claim 14, wherein the electron donor material is glycerol; and the reduction-oxidation indicator material is indigotetrasulfonate.
 21. The method of claim 14, wherein the semiconductor nanoparticles are one of TiO₂, SiC, ZnS, GaN, and Ta₂O₅. 